Influence of pre-oxidation on dual atmosphere effect on AISI 441 interconnects for solid oxide fuel cell applications

Paper i proceeding, 2017

In previous studies an extreme dual atmosphere effect on the airfacing side of AISI 441 at 600°C was observed. However indications showed that pre-oxidation of the material might have a beneficial effect on the corrosion resistance in dual atmosphere. To examine this further we pre-oxidized AISI 441 samples for 0 min, 11 min, 45 min, 180 min and 280 min and subsequently exposed these at 600 °C for 500 h under dual atmosphere conditions. Photographs of the air-facing sides were taken throughout exposure to monitor the corrosion behavior. SEM analysis was performed on all samples after exposure.