Structure and conductivity of acceptor doped La2BaZnO5 and Nd2BaZnO5
Artikel i vetenskaplig tidskrift, 2015
The effect of calcium substitution on the structure and electrical conductivity of Ln(2 - x)Ca(x)BaZnO(5 - delta), Ln = La and Nd, has been studied. Differing trends with respect to dependence of the unit cell volume were observed as a function of Ca substitution. For both series of materials the limit of Ca substitution was estimated to be x approximate to 0.2. The electrical conductivity was studied in the temperature range of 1000-350 degrees C using electrochemical impedance spectroscopy in argon and oxygen atmospheres and via isotherms between 400 and 1000 degrees C as function of oxygen pressure and the water vapour pressure. A marked increase in conductivity of approx. two orders of magnitude was explained by the presence of oxygen vacancies in the calcium doped samples. At pO(2) < 10(-12) atm atm the x = 0.15 materials are predominantly oxygen ion conductors, and La1.85Ca0.15BaZnO5 - delta displays a peak conductivity of 0.002 S cm(-1) at 1000 degrees C. The materials display a rise in conductivity in oxidizing conditions, indicating a significant p-type contribution.
DY
Mixed conductor
Oxide ion conductor
SOFC
SYSTEM
Physical
P176
CHEL C
TRANSPORT
HO
Synthesis
V42
ND
ER
Condensed Matter
1982
Impedance spectroscopy
JOURNAL OF SOLID STATE CHEMISTRY
Chemistry
Physics
OXIDE-ION CONDUCTORS
ELECTROLYTES
PEROVSKITE
Författare
MD khairul Hoque
Chalmers, Kemi och kemiteknik, Energi och material
R. Haugsrud
Universitetet i Oslo
Christopher Knee
Chalmers, Kemi och kemiteknik, Energi och material
Solid State Ionics
0167-2738 (ISSN)
Vol. 272 160-165Ämneskategorier (SSIF 2011)
Oorganisk kemi
Drivkrafter
Hållbar utveckling
DOI
10.1016/j.ssi.2015.02.001