Nanocrystallinity in RuO2 coatings-Influence of precursor and preparation temperature
Artikel i vetenskaplig tidskrift, 2010
The effects of precursor and calcination temperature on the nano morphology of ruthenium dioxide on titanium, prepared from thermal decomposition of aqueous salt solutions were investigated. Transmission electron microscopy. X-ray diffraction, gas porosimetry and cyclic voltammetry showed that lower calcination temperature yielded smaller crystallites. The crystallites were between 6 and 22 nm in diameter. When using ruthenium nitrosyl nitrate the firing temperature had a large impact on the grain size, but for chloride there was only a minor effect in the temperature range 350-550 degrees C. (C) 2009 Elsevier B.V. All rights reserved.
prepared ruthenium oxide
Catalysis
Crystallization
Annealing
films
electrodes
electrocatalysis
X-ray diffraction
Ruthenium nitrosyl nitrate
Författare
C. Malmgren
Mid Sweden University, Sundsvall
Annika Eriksson
Chalmers, Kemi- och bioteknik, Oorganisk miljökemi
Ann Cornell
The Royal Institute of Technology (KTH)
Joakim Bäckström
Mid Sweden University, Sundsvall
Sten Eriksson
Chalmers, Kemi- och bioteknik, Oorganisk miljökemi
Håkan Olin
Mid Sweden University, Sundsvall
Thin Solid Films
0040-6090 (ISSN)
Vol. 518 14 3615-3618Ämneskategorier (SSIF 2011)
Kemi
DOI
10.1016/j.tsf.2009.09.065