Formation and Healing of Voids at the Metal-Oxide Interface in NiAl Alloys
Artikel i vetenskaplig tidskrift, 2009
The present investigation concerns the formation and healing of voids at the metal-oxide interface in beta-NiAl alloys. It is shown that transient cavities form at the metal-oxide interface during the initial stage of isothermal oxidation at 1,050 A degrees C. These voids disappear after a few hours of oxidation, due to their filling with oxide. It is proposed that the filling of the transient voids occurs through cracks in the outer oxide scale. This allows for an oxygen transport into the cavities where a new oxide is created and grows outwards from the metal surface. Pt-containing beta-NiAl alloys that have better resistance to oxide spallation show suppressed formation of cavities and/or a faster filling of voids. This is explained by the enhanced diffusion of Al in these materials.
sulfur segregation
scales
Oxidation
Vacancy injection
cavity formation
Diffusion
cyclic oxidation behavior
interdiffusion
Transmission electron microscopy
adherence
alpha-al2o3
Nickel aluminides
nickel-aluminides
growth
Cavities
pore formation
Författare
Henrik Svensson
Chalmers University of Technology
Pavleta Knutsson
Chalmers, Teknisk fysik, Mikroskopi och mikroanalys
Krystyna Marta Stiller
Chalmers, Teknisk fysik, Mikroskopi och mikroanalys
Oxidation of Metals
0030-770X (ISSN) 1573-4889 (eISSN)
Vol. 71 3-4 143-156Ämneskategorier (SSIF 2011)
Metallurgi och metalliska material
DOI
10.1007/s11085-008-9132-z