SOx storage and release kinetics for ceria-supported Pt
Journal article, 2009
The SOx storage and release kinetics on CeO2 have been studied by lean SOx adsorption and temperature programmed desorption for different pairwise configurations of individual monolith samples, i.e., Pt/CeO2 + SiO2, Pt/SiO2 + CeO2, CeO2 + Pt/SiO2 and CeO2 + SiO2. In the case of sole ceria, SOx adsorption proceeds both via SO2 and SO3 adsorption although the latter channel is kinetically favored. Hence, the rate of SO2 oxidation is crucial for the overall SOx storage kinetics. It is also found that physical contact between Pt and ceria is important for the storage process. This is attributed to efficient transport routes for SOx (surface diffusion and spill-over processes) and/or specific adsorption sites at the platinum–ceria interface. The main route for SOx release is found to be thermal decomposition where the effect of platinum is minor, although an indirect effect cannot be ruled out. Different mechanistic scenarios for SOx adsorption are discussed, which may serve as a guide for future experiments.
CeO2
CATALYST
Sulfur trap
Adsorption
Noble metal-support interaction
SO2 oxidation
TRAPS
Desorption
Pt
SULFUR
NO
Author
Markus Happel
Friedrich-Alexander-Universität Erlangen-Nürnberg
Lisa Kylhammar
Chalmers, Chemical and Biological Engineering, Applied Surface Chemistry
Competence Centre for Catalysis (KCK)
Per-Anders Carlsson
Chalmers, Chemical and Biological Engineering, Applied Surface Chemistry
Competence Centre for Catalysis (KCK)
J. Libuda
Friedrich-Alexander-Universität Erlangen-Nürnberg
Henrik Grönbeck
Chalmers, Applied Physics, Chemical Physics
Competence Centre for Catalysis (KCK)
Magnus Skoglundh
Chalmers, Chemical and Biological Engineering, Applied Surface Chemistry
Competence Centre for Catalysis (KCK)
Applied Catalysis B: Environmental
0926-3373 (ISSN) 1873-3883 (eISSN)
Vol. 91 3-4 679-682Driving Forces
Sustainable development
Areas of Advance
Nanoscience and Nanotechnology
Transport
Energy
Materials Science
Subject Categories (SSIF 2011)
Physical Chemistry
Other Engineering and Technologies not elsewhere specified
Other Materials Engineering
DOI
10.1016/j.apcatb.2009.07.002