InPBi Single Crystals Grown by Molecular Beam Epitaxy
Journal article, 2014
InPBi was predicted to be the most robust infrared optoelectronic material but also the most difficult to synthesize within In-VBi (V 5 P, As and Sb) 25 years ago. We report the first successful growth of InPBi single crystals with Bi concentration far beyond the doping level by gas source molecular beam epitaxy. The InPBi thin films reveal excellent surface, structural and optical qualities making it a promising new III-V compound family member for heterostructures. The Bi concentration is found to be 2.4 +/- 0.4% with 94 +/- 5% Bi atoms at substitutional sites. Optical absorption indicates a band gap of 1.23 eV at room temperature while photoluminescence shows unexpectedly strong and broad light emission at 1.4-2.7 mmwhich can't be explained by the existing theory.
GAASN
Multidisciplinary Sciences
P1555
BI
EMISSION
1971
GAP
AN PJ
ALLOYS
V9
SOLID STATE COMMUNICATIONS
BISMUTH
ABSORPTION
PHOSPHIDE
Author
K. Wang
Shanghai Institute of Microsystem and Information Technology Chinese Academy of Sciences
Yi Gu
Shanghai Institute of Microsystem and Information Technology Chinese Academy of Sciences
H. F. Zhou
Shanghai Institute of Microsystem and Information Technology Chinese Academy of Sciences
L. Y. Zhang
Shanghai Institute of Microsystem and Information Technology Chinese Academy of Sciences
C. Z. Kang
Qufu Normal University
M. J. Wu
Paul Drude Institut fur Festkorperelektronik
W. W. Pan
Shanghai Institute of Microsystem and Information Technology Chinese Academy of Sciences
P. F. Lu
Beijing University of Posts and Telecommunications
Q. Gong
Shanghai Institute of Microsystem and Information Technology Chinese Academy of Sciences
Shu Min Wang
Chalmers, Microtechnology and Nanoscience (MC2), Photonics
Scientific Reports
2045-2322 (ISSN)
Vol. 4 5449Subject Categories (SSIF 2011)
Nano Technology
DOI
10.1038/srep05449