Improved cationic stoichiometry and insulating behavior at the interface of LaAlO3/SrTiO3 formed at high oxygen pressure during pulsed-laser deposition

Journal article, 2011

Medium-energy ion spectroscopy, MEIS, and scanning transmission electron microscopy, STEM, were used to correlate the atomic structure of LaAlO3/SrTiO3 interfaces with their electrical properties. Interfaces were prepared at high (5x10(-2) mbar) and low (10(-4) mbar) oxygen pressure by pulsed-laser deposition. The high-oxygen-pressure heterostructures were insulating for all thicknesses while the low-oxygen-pressure ones became metallic for thicknesses above 4 unit cells. MEIS data show enhancement of the Sr surface peak and suppression of the La one in interfaces prepared at low oxygen pressure, which is interpreted as a La-Sr intermixing. The effect was considerably smaller in high-oxygen-pressure samples. Analysis of high-angle annular-dark-field STEM images of the LAO films also indicates intermixing between La and Sr in low-oxygen-pressure samples, supporting MEIS data. Our results reveal the important role of oxygen pressure on the formation of the interface electron gas. Copyright (C) EPLA, 2011